dc.identifier.citationZhang, H., Wang, P., & Yang, J. (2014). Self-healing epoxy via epoxy–amine chemistry in dual hollow glass bubbles. Composites Science and Technology, 94, 23-29.en_US
dc.description.abstractEtched hollow glass bubbles (HGBs) with through-holes at micron level were used as micro-containers for epoxy and amine solution to realize the self-healing functionality in epoxy matrix. The average diameter, the average shell thickness, as well as the cavity inside the shell were investigated. In order to check the mechanical robustness and the rupturability of the HGBs, micro-compression tests of single HGB were conducted to measure their mechanical responses, which reveal the relatively high compressive strength and brittle feature. A new type of self-healing epoxy was developed based on the dual HGB carriers and the self-healing performance was optimized systematically to obtain better healing behavior. It is found the highest healing efficiency of about 62% was achieved at 50 °C for 24 h when 12.5 - 15.0 wt% healing agent carriers was incorporated at the optimized ratio of 4 : 1 for epoxy loaded HGBs (HGB-E) to amine loaded HGBs (HGB-A). It is also found that the healing efficiency increased with increased healing duration at 50 °C. In addition, the fracture toughness is improved and the tensile modulus keeps constant while the tensile strength is deteriorated by the incorporation of the carriers.en_US
dc.description.sponsorshipASTAR (Agency for Sci., Tech. and Research, S’pore)
dc.relation.ispartofseriesComposites science and technologyen_US
dc.rights© 2014 Elsevier Ltd. This is the author created version of a work that has been peer reviewed and accepted for publication by Composites Science and Technology, Elsevier Ltd. It incorporates referee’s comments but changes resulting from the publishing process, such as copyediting, structural formatting, may not be reflected in this document. The published version is available at: [http://dx.doi.org/10.1016/j.compscitech.2014.01.009]en_US
dc.subjectDRNTU::Engineering::Aeronautical engineering::Aerodynamics
dc.titleSelf-healing epoxy via epoxy–amine chemistry in dual hollow glass bubblesen_US
dc.typeJournal Article
dc.contributor.schoolSchool of Mechanical and Aerospace Engineeringen_US
dc.description.versionAccepted versionen_US

Files in this item


This item appears in the following Collection(s)

Show simple item record