Title: Tin whiskers growth of SnAgIn solder on Kovar substrate with Au/Ni plating
Authors: Li, Qingqian
Chan, Y. C.
Chen, Zhong
Keywords: DRNTU::Engineering::Materials::Electronic packaging materials
Issue Date: 2014
Source: Li, Q., Chan, Y. C. ,& Chen, Z. (2014). Tin whiskers growth of SnAgIn solder on Kovar substrate with Au/Ni plating. Journal of materials science : materials in electronics, 25(3), 1222-1227.
Series/Report no.: Journal of materials science : materials in electronics
Abstract: In this research, the interactions of SnInAg solder on Kovar leadframes (Fe29Ni17Co) with Au/Ni UMB was studied, to reveal the whiskers growth mechanism. Samples were prepared by reflow process and aging, with SnInAg solder paste on the substrate. Scanning electron microscope was used to observe the morphology and the cross-sectioned structure of the whiskers. Focused ion-beam was used for the preparation of the transmission electron microscope (TEM) samples, and energy dispersive X-ray and TEM were then used to distinguish the different intermetallic compound (IMC) phases. It was found that, a special solder thickness range would be needed for the growth of whiskers. The root cause of this strip whiskers growth region was studied. It is worthy to mention that, the Sn–Cu reactions, which was reported by many former researches, was not the main source of the compressive stress here. It was found that the Au–Sn reactions, the IMCs transformation during the aging process, and the oxidation layer growth were dominating the whiskers growth. Effects of cracks on the whiskers growth were carefully observed and discussed, and it was found that cracks under a certain width could exempt the breaking of the oxidation layer at the solder surface, thus help the whiskers growth. On the other hand, wide cracks might accommodate the deformation of the solder layer and prohibit the whiskers from being erupted out.
URI: https://hdl.handle.net/10356/102482
http://hdl.handle.net/10220/24288
DOI: http://dx.doi.org/10.1007/s10854-014-1713-9
Rights: © 2014 Springer Science+Business Media New York.
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:MSE Journal Articles

Google ScholarTM

Check

Altmetric

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.