dc.identifier.citationSujakhu, S., Castagne, S., Sakaguchi, M., Kasvayee, K. A., Ghassemali, E., Jarfors, A. E. W., et al. (2017). On the fatigue damage micromechanisms in Si-solution–strengthened spheroidal graphite cast iron. Fatigue & Fracture of Engineering Materials & Structures, in press.en_US
dc.description.abstractGraphite nodules in Spheroidal graphite cast iron (SGI) play a vital role in fatigue crack initiation and propagation. The graphite nodule growth morphology can go through transitions to form degenerated graphite nodules other than spheroidal graphite nodules in SGI microstructure. These graphite nodules significantly influence damage micromechanisms on SGI and could act differently. Most of the damage mechanism studies on SGI were focused on the role of spheroidal graphite nodules on the stable crack propagation region. The roles of degenerated graphite nodules on SGI damage mechanisms were not frequently studied. In this work, fatigue crack initiation and propagation tests were conducted on EN-GJS-500-14 and observed under SEM to understand damage mechanisms of different graphite forms. Crack initiation tests showed dominant influence of degenerated graphite nodules where early cracks initiated in the microstructure. Most of the spheroidal graphite nodules were unaffected at the early crack initiation stage; some of them showed decohesion from the ferrite matrix and internal cracking. At the crack propagation region, graphite-ferrite matrix decohesion was the frequent damage mechanism observed with noticeable crack branching around graphite nodules and the crack passing through degenerated graphite nodules. Finally, graphite nodules after decohesion acted like voids which grew and coalesced to form microcracks eventually causing rapid fracture of the remaining section.en_US
dc.description.sponsorshipMOE (Min. of Education, S’pore)en_US
dc.format.extent30 p.en_US
dc.relation.ispartofseriesFatigue & Fracture of Engineering Materials & Structuresen_US
dc.rights© 2017 Wiley Publishing Ltd. This is the author created version of a work that has been peer reviewed and accepted for publication by Fatigue & Fracture of Engineering Materials & Structures, Wiley Publishing Ltd. It incorporates referee’s comments but changes resulting from the publishing process, such as copyediting, structural formatting, may not be reflected in this document. The published version is available at: [http://dx.doi.org/10.1111/ffe.12723].en_US
dc.subjectSpheroidal graphite cast ironen_US
dc.subjectDamage micromechanismsen_US
dc.titleOn the fatigue damage micromechanisms in Si-solution–strengthened spheroidal graphite cast ironen_US
dc.typeJournal Article
dc.contributor.schoolSchool of Mechanical and Aerospace Engineeringen_US
dc.description.versionAccepted versionen_US

Files in this item


This item appears in the following Collection(s)

Show simple item record