Title: Effect of heat treatment on fatigue crack initiation of laser powder bed fusion stainless steel 316L
Authors: Zhang, Meng
Sun, Chen-Nan
Zhang, Xiang
Goh, Phoi Chin
Wei, Jun
Hardacre, David
Li, Hua
Keywords: Stainless Steel 316L
Crack Initiation
DRNTU::Engineering::Mechanical engineering
Issue Date: 2018
Source: Zhang, M., Sun, C.-N., Zhang, X., Goh, P. C., Wei, J., Hardacre, D., & Li, H. (2018). Effect of heat treatment on fatigue crack initiation of laser powder bed fusion stainless steel 316L. MATEC Web of Conferences, 165, 22006-. doi:10.1051/matecconf/201816522006
Series/Report no.: MATEC Web of Conferences
Abstract: Laser powder bed fusion (L-PBF) is an emerging additive manufacturing technique for building structural components. L-PBF processing defects, such as lack of fusion pores, promote fatigue crack initiation and shorten the fatigue life. With well-controlled processing, critical pores can be avoided such that the microstructure-driven intergranular crack initiation mode becomes operative. In this work, the fatigue crack initiation behaviours of as-built and solution annealed L-PBF stainless steel 316L were studied. Crack initiation of the as-built samples is driven by de-bonding of the dendritic grain boundaries. High temperature annealing results in the formation of thermally-induced defects, possibly via the reheat cracking mechanism and the nucleation of pre-existing gas pores. As heat treating could have led to recrystallization and annihilation of the original grain boundary defects, the thermally-induced defects became the new sites for crack initiation. In addition, heat treatment incurred significant reduction in yield strength, such that the interaction of fatigue and ratcheting strain accumulation dominated the deformation behaviour of the material. The resulting fatigue strength in the finite life regime was reduced by about 13% but the fatigue endurance limit was not affected.
URI: https://hdl.handle.net/10356/88267
http://hdl.handle.net/10220/45679
DOI: http://dx.doi.org/10.1051/matecconf/201816522006
Rights: © 2018 The Author(s) (MATEC Web of Conferences) (Published by EDP Sciences). This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. (http://creativecommons.org/licenses/by/4.0/).
metadata.item.grantfulltext: open
metadata.item.fulltext: With Fulltext
Appears in Collections:MAE Journal Articles

Google ScholarTM

Check

Altmetric

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.