Please use this identifier to cite or link to this item: https://hdl.handle.net/10356/101825
Title: Highly enhanced sinterability of fine-grained Ba0.6Sr0.4TiO3−MgO bulk ceramics and in-situ nanocomposite thick films
Authors: Chan, Helen Lai-Wa
Zhang, Hongfang
Kong, Ling Bing
Mak, Chee-Leung
Kwok, Kin-Wing
Wang, Yu
Keywords: DRNTU::Engineering::Materials::Ceramic materials
Issue Date: 2014
Source: Zhang, H., Kong, L. B., Mak, C.-L., Kwok, K.-W., Wang, Y.,& Chan, H. L.-W. (2014). Highly enhanced sinterability of fine-grained Ba0.6Sr0.4TiO3−MgO bulk ceramics and in-situ nanocomposite thick films. Ceramics international, 40(7), 10475-10481.
Series/Report no.: Ceramics international
Abstract: Well-developed, dense and fine-grained MgO–(Ba0.6Sr0.4)TiO3 with 40 wt% MgO content (denoted as BST–MgO) bulk ceramics were fabricated by high-energy ball mechanochemical technique using a hybrid processing. Based on this technique, the fabrication temperature was as low as 1200 °C i.e., 200 °C lower than that required by using conventional solid-state process. At the same time, dense, homogeneous and crack-free ceramic–ceramic 0–3 nanocomposite BST–MgO thick film was obtained at 700 °C using the spin-coating method. At 10 kHz and room temperature, the BST–MgO bulk ceramics exhibited a moderate dielectric constant of about 500 and low loss tangent of less than 0.005; while for the nanocomposite thick films, the dielectric constant and loss tangent were about 140 and less than 0.03 (at 100 kHz) respectively. In addition, both the bulk ceramics and thick film show a broad and diffused phase transition. The dielectric room-temperature tunabilities measured at 100 kHz were found to be 4% at 1.5 kV/mm for the bulk ceramic, and 17% at 10 kV/mm for nanocomposite thick film.
URI: https://hdl.handle.net/10356/101825
http://hdl.handle.net/10220/24175
ISSN: 0272-8842
DOI: 10.1016/j.ceramint.2014.03.018
Rights: © 2014 Elsevier Ltd and Techna Group S.r.l. This is the author created version of a work that has been peer reviewed and accepted for publication by Ceramics International, Elsevier Ltd. It incorporates referee’s comments but changes resulting from the publishing process, such as copyediting, structural formatting, may not be reflected in this document. The published version is available at: [http://dx.doi.org/10.1016/j.ceramint.2014.03.018].
Fulltext Permission: open
Fulltext Availability: With Fulltext
Appears in Collections:MSE Journal Articles

Google ScholarTM

Check

Altmetric


Plumx

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.