Title: Silica nanoparticle gelled ionic electrolyte for dye sensitized solar cells
Authors: Huang, Shengnan
Wang, Xiu
Wong, Chee Cheong
Keywords: DRNTU::Engineering::Materials::Nanostructured materials
Issue Date: 2013
Source: Huang, S., Wang, X., & Cheong Wong, C. (2013). Silica nanoparticle gelled ionic electrolyte for dye sensitized solar cells. Nanoscience and Nanotechnology Letters, 5(5), 542-545.
Series/Report no.: Nanoscience and nanotechnology letters
Abstract: Gelled ionic electrolyte was synthesized with silica nanoparticles and binary ionic liquid electrolyte. Symmetric cells with varied silica contents were tested using electrochemical impedance spectroscopy to study the effect of silica nanoparticles on counter electrode. Dye sensitized solar cells consisting of binary ionic electrolytes with different silica contents were fabricated. I–V test under various light intensities and electrochemical impedance spectroscopy at various biases were conducted to study the effect of silica nanoparticles on charge transfer at the counter electrode/electrolyte interface and on charge transport in the electrolyte. It was observed that charge transfer resistance decreased and electron recombination lifetime increased with the increasing of silica content. Both photocurrent and power conversion efficiency initially decreased and then increased resulting in minimum values at around 9 wt%. This observation could be attributed to the change in dominant charge transport mechanisms: with addition of silica nanoparticles, physical diffusion decreases, while exchange reaction based charge transport in electrolyte is enhanced and the enhancement of exchange reaction overcomes the exacerbation of physical diffusion at around 9 wt%. With the findings above, the charge transport mechanism can be further studied to optimize the efficiency of devices with gelled ionic electrolyte.
ISSN: 1941-4900
DOI: 10.1166/nnl.2013.1577
Rights: © 2013 American Scientific Publishers.
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:MSE Journal Articles

Citations 20

Updated on Jul 13, 2020

Citations 20

Updated on Mar 6, 2021

Page view(s)

Updated on Jun 27, 2022

Google ScholarTM




Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.