Title: Induction transient liquid phase bonding of Inconel 718 with the nickel-based sintered brazing preform
Authors: Yan, Guangxu
Nagarajan, Balasubramanian
Bhowmik, Ayan
Tan, Sung Chyn
Xu, Ray
Tan, Ming Jen
Keywords: Engineering::Mechanical engineering
Issue Date: 2019
Source: Yan, G., Nagarajan, B., Bhowmik, A., Tan, S. C., Xu, R. & Tan, M. J. (2019). Induction transient liquid phase bonding of Inconel 718 with the nickel-based sintered brazing preform. Applied Surface Science, 473, 1024-1037. https://dx.doi.org/10.1016/j.apsusc.2018.12.187
Project: M-RT3.2
Journal: Applied Surface Science
Abstract: Generally, transient liquid phase (TLP) bonding is conducted with an overdose of filler metal in a vacuum furnace that necessitates excessive post machining. Recently, a new form of filler metal, the sintered brazing preforms (SBP) has been introduced to achieve a neat TLP bonding joint, which undergoes partial melting and retains its original shape. This paper studies the microstructure and mechanical properties of induction TLP bonding (IB) of the Inconel 718 using nickel-based SBP. Firstly, the surface roughness effect on the tensile bonding strength of the brazed joint was investigated. Further, a comparative study between IB and furnace TLP bonding (FB) on the microstructure and mechanical properties of the TLP joints was performed. The results clearly show that neat bonding joints can be obtained through the IB of Inconel 718 using nickel-based SBP. Besides, the strongest tensile bonding strength (240.76 MPa) of the SBP joint after IB was achieved with an optimal bonding surface roughness of around 0.9 μm (Ra). The strength was approximately 16% higher than that of the SBP joint after FB. Furthermore, the IB could accelerate the diffusion process, leading to fewer porosities and borides in the SBP, and a lesser amount of precipitates in the precipitation layer than that after FB.
URI: https://hdl.handle.net/10356/150579
ISSN: 0169-4332
DOI: 10.1016/j.apsusc.2018.12.187
Rights: © 2018 Elsevier B.V. All rights reserved
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:MAE Journal Articles

Page view(s)

36
Updated on Sep 26, 2021

Google ScholarTM

Check

Altmetric


Plumx

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.