Title: Application of AlMgGaLi foil for joining copper to SiCp/Al-MMCs for high-temperature and high-power electronics
Authors: Chen, Biqiang
Chen, Zhong
Du, Zehui
Zhang, Guifeng
Keywords: Engineering::Materials
Issue Date: 2019
Source: Chen, B., Chen, Z., Du, Z. & Zhang, G. (2019). Application of AlMgGaLi foil for joining copper to SiCp/Al-MMCs for high-temperature and high-power electronics. Applied Physics A: Materials Science and Processing, 125(8), 581-. https://dx.doi.org/10.1007/s00339-019-2884-2
Journal: Applied Physics A: Materials Science and Processing
Abstract: A novel lead-free foil (AlMgGaLi) with a melting point of 398.3 ~ 414.8 °C was developed for active soldering of copper to aluminum matrix composite. The effect of joining pressure on the microstructure, interface wetting and shear strength of the dissimilar joints was analyzed. When the joining pressure increased to 1 MPa, an Al-based solid solution with an atomic composition of 89.62% Al, 6.5% Mg, 3.1% O, 0.46% Cu, 0.23% Ga and 0.09% Si was formed within the bond seam and the thickness of the transition layer with copper dissolution was approximately 4.9 μm. The joining pressure improved the interfacial wettability of the dissimilar joint by enhancing mutual diffusion with a shortened interface layer, tailored the runout and the formation of bond seam, and controlled an appropriate thickness of the copper dissolution transition layer. Sound joint with a maximum shear strength of 94 MPa (~ 80% of parent composites) is achievable at 450 °C using the joining pressure of 1 MPa. The failure mechanism of the joints with the AlMgGaLi foil under shear stress has been revealed from the analysis on the interface layers of the joints with SEM/EDX/XRD. Our studies provide an important guideline for using an AlMgGaLi and other similar fillers for a successfully joining of copper to Al-MMCs for high-temperature and high-power electronic devices.
URI: https://hdl.handle.net/10356/151487
ISSN: 0947-8396
DOI: 10.1007/s00339-019-2884-2
Rights: © 2019 Springer-Verlag GmbH Germany, part of Springer Nature. All rights reserved.
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:MSE Journal Articles

Page view(s)

63
Updated on Nov 28, 2021

Google ScholarTM

Check

Altmetric


Plumx

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.