Title: Bonding temperature effects on the wide gap transient liquid phase bonding of Inconel 718 using BNi-2 paste filler metal
Authors: Yan, Guangxu
Bhowmik, Ayan
Nagarajan, Balasubramanian
Song, Xu
Tan, Sung Chyn
Tan, Ming Jen
Keywords: Engineering::Mechanical engineering
Issue Date: 2019
Source: Yan, G., Bhowmik, A., Nagarajan, B., Song, X., Tan, S. C. & Tan, M. J. (2019). Bonding temperature effects on the wide gap transient liquid phase bonding of Inconel 718 using BNi-2 paste filler metal. Applied Surface Science, 484, 1223-1233. https://dx.doi.org/10.1016/j.apsusc.2019.04.070
Project: M-RT3.2
Journal: Applied Surface Science
Abstract: Transient liquid phase (TLP) bonding of Inconel 718 with BNi-2 filler metal has traditionally been carried out using thin filler metal (narrow gap) to achieve complete eutectic-free isothermal solidification layer joints. However, for the aerospace components with relatively large cracks or worn areas where a large amount of filler metal is needed, narrow gap TLP bonding is insatiable to meet the bonding requirements. In this paper, wide gap TLP bonding of Inconel 718 with the BNi-2 paste filler metal was carried out in a vacuum furnace. The bonding temperature effects on the interfacial microstructure, phase evolution and the mechanical properties of the bonded joints were investigated. It was found that the ultimate tensile bonding strength increased by 98% as the bonding temperature increased from 1015 °C to 1150 °C and the joint with the maximum tensile strength of 482 MPa was achieved after bonding at 1150 °C for 15 mins. However, more adverse heating was induced on the base metal of the joint under a higher bonding temperature. In addition, increasing bonding temperature from 1015 °C to 1150 °C improved the local plasticity of the bonded joints owing to the reduction of the homogeneously distributed Ni₃B type borides to a more heterogeneous distribution of borides.
URI: https://hdl.handle.net/10356/151524
ISSN: 0169-4332
DOI: 10.1016/j.apsusc.2019.04.070
Rights: © 2019 Published by Elsevier B.V. All rights reserved.
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:MAE Journal Articles

Page view(s)

57
Updated on Nov 30, 2021

Google ScholarTM

Check

Altmetric


Plumx

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.