Title: Synthesis and characterization of photocatalytic zinc oxide thin films
Authors: Liu, Yiwei.
Keywords: DRNTU::Engineering
Issue Date: 2009
Abstract: Photocatalytic zinc oxide (ZnO) thin films were synthesized and characterized on glass. First, a stable zinc peroxide (ZnO2) nano-particle colloid was produced. The 4 reagents were zinc acetate dihydrate, DI water, H2O2 and PEG 200. The colloid was spin coated and spray coated onto glass substrates, then heated at 450oC for 1hr to obtain ZnO thin films. XRD analysis was conducted and confirmed correct ZnO crystals were obtained. Coating development was carried out to determine a process for obtaining a good coating quality. Transmittance, haze and clarity were measured to verify coating quality. Super-hydrophilicity effect was clearly present under UV irradiation for spin coated sample. Very slow oxidation rate under UV irradiation was measured over 64 hours for all samples.
URI: http://hdl.handle.net/10356/17996
Rights: Nanyang Technological University
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:EEE Student Reports (FYP/IA/PA/PI)

Files in This Item:
File Description SizeFormat 
eB6094-081.pdf
  Restricted Access
3.61 MBAdobe PDFView/Open

Page view(s)

229
checked on Sep 26, 2020

Download(s)

10
checked on Sep 26, 2020

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.