Please use this identifier to cite or link to this item: https://hdl.handle.net/10356/43855
Title: Inorganic nanowire based solar cells
Authors: Fu, Kunwu.
Keywords: DRNTU::Engineering::Materials::Energy materials
Issue Date: 2011
Abstract: 1-D nanostructure network of tin oxide has advantages in dye-sensitized solar cell because of its direct charge transport channel, higher electron mobility and better long-term stability, compared with the conventionally used TiO2 nanoparticle. This project focuses on growth of tin oxide 1-D nanostructure network via Vapor-liquid-solid method and study the application of tin oxide material in dye-sensitized solar cell. Tin oxide and graphite mixed powders were used as source material to grow nanowires with different lengths and diameters on gold-catalysed substrates. SEM, Alpha surface profiler, EDX and XRD were used to characterize the nanowire film morphology, thicknesses, nanowire diameters, compositions and crystal structures. Liquid dye-sensitized solar cells were fabricated from the tin oxide nanowire films and the efficiencies were tested under 1 Sun AM1.5 global condition. The effect of counter electrode Pt-coating’s amount, nanowire length and nanowire diameter on the solar cell efficiency were studied. Optimum amount of 50μL of 8mM H2PtCl6 was found to give the best efficiency. Nanowire film thickness and diameter were modified to achieve efficiency level at 0.18%. Antimony doping technique was also evaluated for its effect on cell efficiency. The back-illumination cell structure and hetero-junction formed at the interface between the silicon substrate and the tin oxide put a limit on the highest cell efficiency value to 0.18%.
URI: http://hdl.handle.net/10356/43855
Rights: Nanyang Technological University
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:MSE Student Reports (FYP/IA/PA/PI)

Files in This Item:
File Description SizeFormat 
Final Year Project Report - Fu Kunwu.pdf
  Restricted Access
2.93 MBAdobe PDFView/Open

Page view(s) 50

244
Updated on Dec 1, 2020

Download(s)

12
Updated on Dec 1, 2020

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.