dc.description.abstractThis Final Year Project shows the effect of carbon content on the heat treatment process; and how the interlamellar spacing differs under prolong heat treatment with different carbon compositions. The purpose of the project is to investigate the relation and effects between the different carbon content and heat treatment time on the interlamellar spacing. Microstructures images were obtained by using the Scanning Electron Microscope (SEM) and the lamellar spacing were measured using software called ImageJ 1.37v. For this project, two different compositions of steel specimens were used, 0.77% and 1%, whereby both were heat treated at the temperatures of 0, 4, 8, 16, 24 and 48 hours. A series of measurements were collected to determine the average spacing of the interlamellar spacing. Charts were plotted to evaluate pearlite structure at different heat treatment hours. From the results and analysis, it is observed that under extended heat treatment, the cementite plates will form globules of spheroids. Fine pearlite structures are found to have smaller interlamellar spacing. Pearlite tends to coarsen in the high carbon content steel. Hence, steel that has lower carbon content (0.77%C) has a faster spheroidization rate. The interlamellar spacing for this steel is also larger than the higher carbon content steel (1%C).en_US
dc.format.extent60 p.en_US
dc.language.isoenen_US
dc.rightsNanyang Technological University-
dc.subjectDRNTU::Engineering::Materialsen_US
dc.titleEffect of carbon content on the heat treatment processen_US
dc.typeFinal Year Project (FYP)en_US
dc.contributor.supervisorOh Joo Tienen_US
dc.contributor.schoolSchool of Materials Science and Engineeringen_US
dc.description.degreeBachelor of Engineering (Materials Engineering)en_US
item.fulltextWith Fulltext-
item.grantfulltextrestricted-
Appears in Collections:MSE Student Reports (FYP/IA/PA/PI)
Files in This Item:
File Description SizeFormat 
MSE10-171.pdf
  Restricted Access
17.09 MBAdobe PDFView/Open

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.