dc.description.abstractAged wire electro-exploded, platinum nanopowder has been characterized by differential scanning calorimetry (DSC) and a comparative analysis made between virgin and aged platinum nanopowder. The platinum nanopowder had a wide distribution of particle sizes between 5 to 250 nm and a purity of 99.9%. The powder was highly agglomerated, with a high density of defects. For virgin platinum nanopowder, the differential scanning calorimetry (DSC) results indicated that there are two endothermic reactions at about 100°C and 350°C, an exothermic reaction within the temperature range of 173.4°C to 198.57°C. The two reaction peaks are likely due to melting and crystallization. The activation energy of the virgin platinum was about 96±5% KJ/mol for exothermic peak. The DSC indicated that the peak temperature of exothermic peak for aged Platinum nanopowder appeared to be shifted up by 2% when it was pre-sintered at 100°C for up to five hours. When it was aged for eight hours, the peak temperature was increased by 4% compared to normal powder. According to the finding, the calculated activation energy for age platinum nanopowder was 97KJ/mol. It was no difference comparing with virgin platinum nanopowder.en_US
dc.format.extent55 p.en_US
dc.language.isoenen_US
dc.rightsNanyang Technological University
dc.subjectDRNTU::Engineering::Materials::Nanostructured materialsen_US
dc.titleAn investigation of the aging of electro exploded platinum nanopowderen_US
dc.typeFinal Year Project (FYP)en_US
dc.contributor.supervisorChristopher Shearwooden_US
dc.contributor.schoolSchool of Mechanical and Aerospace Engineeringen_US
dc.description.degreeBachelor of Engineering (Mechanical Engineering)en_US
item.grantfulltextrestricted-
item.fulltextWith Fulltext-
Appears in Collections:MAE Student Reports (FYP/IA/PA/PI)
Files in This Item:
File Description SizeFormat 
FYP Report (Final).pdf
  Restricted Access
Main article997.73 kBAdobe PDFView/Open

Page view(s)

203
Updated on Nov 30, 2020

Download(s) 5

11
Updated on Nov 30, 2020

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.