Title: Fabrication and characterization of organic single crystal field-effect transistors
Authors: Zhang, Keke
Keywords: DRNTU::Engineering::Materials::Organic/Polymer electronics
Issue Date: 2013
Abstract: Rubrene, a poly-aromatic hydrocarbon, is studied in this thesis. Purity of commercial rubrene powder and rubrene single crystals, grown by PVT technique, were investigated by means of high performance liquid chromatography and mass spectroscopy. High quality rubrene single crystals were used to fabricate Si / SiO2 and air-gap transistors based on pre-patterned PDMS stamp. On such transistor architecture, rubrene single crystal shows mobility as high as 19 cm2/Vs. Electrical properties displayed dramatic changes in the presence of different gas environments. The effects of O2, H2, CO, NO2 and H2S gas were studied. In the presence of oxidative gas, mobility remains high while in reductive gas, mobility drops to a lower value. The high mobility of rubrene FETs measured in ambient environment may not reflect its intrinsic behavior but is a consequence of the oxidation states on the rubrene surface. Femtosecond pump-probe experiments were performed on rubrene single crystals. Both direct and thermally activated singlet fission were observed by transient absorption measurements under different excitation wavelengths. Polarons were proved to form from higher excited singlet state not the relaxed first singlet state. 85% of polarons recombined in 1 ns after generation. The remaining polarons lasted longer than 1 ms, which may contribute to high mobility in rubrene single crystals.
URI: http://hdl.handle.net/10356/52497
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:MSE Theses

Files in This Item:
File Description SizeFormat 
Zhang, Keke P.h.D. Thesis.pdf
  Restricted Access
Main thesis6.65 MBAdobe PDFView/Open

Page view(s)

309
Updated on Nov 25, 2020

Download(s)

25
Updated on Nov 25, 2020

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.