Title: Analyses of failures in welded crane rail
Authors: Chen, Wenbin.
Keywords: DRNTU::Engineering::Mechanical engineering::Mechanics and dynamics
Issue Date: 2013
Abstract: Crane rail have been playing critical role as foundation for container transportation around the world. Recent fractured rail was discovered after few months of operation after cleared with ultrasonic test. In this report, it analyses failure root causes of crane rail, through various characterization techniques, Scanning Electron Microscopy, Energy Dispersive X-ray Spectrometry and Optical Microscopy. It was determined that presence of martensite in heat affected zone link to hydrogen-induce cold crack was the agitation factor for fracture. To overcome this problem and increase service cycle for crane rail, recommendation for pre-weld and post-weld heat treatment to achieve uniform microstructure.
URI: http://hdl.handle.net/10356/53252
Rights: Nanyang Technological University
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:MAE Student Reports (FYP/IA/PA/PI)

Files in This Item:
File Description SizeFormat 
mb475.pdf
  Restricted Access
3.1 MBAdobe PDFView/Open

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.