dc.contributor.authorToh, Xin Hui
dc.date.accessioned2015-05-22T07:30:21Z
dc.date.available2015-05-22T07:30:21Z
dc.date.copyright2015en_US
dc.date.issued2015
dc.identifier.urihttp://hdl.handle.net/10356/64057
dc.description.abstractIn aerospace industry, aluminum alloys have been the material of choice when it comes to building the fuselage, wing and supporting structure of modern passenger aircraft, military cargo and transport since 1930 [1]. Aluminum alloys are chosen due to their well-known performance characteristics, known fabrication costs, design experience, resistance to corrosion and high strength to weight ratio that will increase payload and save in fuel consumption. They usually undergo anodizing as a surface treatment to further enhance their protection against corrosion and to increase adhesion to paint. However, it has been understood that most paint adhesion problems are mainly due to delamination between the primer and the sealed anodic surface. Therefore, in this project, AA2024 specimens will be anodized under MIL-A-8625F Type II to understand the adhesion and characterization of the interface between the anodized aluminum alloy surface and two standard commercial aerospace primers A) with chromate, and B) chromate free. Three intrinsic factors have been designed to be taken into consideration for our experiments. They are the temperature used during the experiment, the presence of nickel incorporated in the sealing process and the presence of chromate in the primer. Two factors have been identified to be significant. The presence of nickel in the sealing process and chromate in the primer has shown to be more beneficial to adhesion. As such, it is vital to locate nickel further in the anodized oxide layer as the results from Scanning Electron Microscope (SEM) are not able to detect the nickel in the top sample surface as the total average over the surface is lower than 5 atomic percent.en_US
dc.format.extent46 p.en_US
dc.language.isoenen_US
dc.rightsNanyang Technological University
dc.subjectDRNTU::Engineering::Aeronautical engineering::Aircraften_US
dc.titleAdhesion and characterization of the interface between aerospace standard primer and anodized aluminium alloyen_US
dc.typeFinal Year Project (FYP)en_US
dc.contributor.supervisorLi Huaen_US
dc.contributor.schoolSchool of Mechanical and Aerospace Engineeringen_US
dc.description.degreeBachelor of Engineering (Mechanical Engineering)en_US
dc.contributor.organizationA*STAR Singapore Institute of Manufacturing Technologyen_US
item.fulltextWith Fulltext-
item.grantfulltextrestricted-
Appears in Collections:MAE Student Reports (FYP/IA/PA/PI)
Files in This Item:
File Description SizeFormat 
B335 (U1121002A).pdf
  Restricted Access
15.06 MBAdobe PDFView/Open

Page view(s)

108
Updated on Jan 24, 2021

Download(s)

13
Updated on Jan 24, 2021

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.