Title: Stress intensity factor of cracks in lugs
Authors: Li, Wen Hao
Keywords: DRNTU::Engineering::Aeronautical engineering::Materials of construction
Issue Date: 2015
Abstract: This project explores the experimental determination of the stress intensity factor of straight aircraft attachment lugs made of aluminium alloy Al7075-T651. The specimen used for tests has two initial quarter corner elliptical part through cracks fabricated diametrically opposite each other at the sides of the lug hole. As such, the crack propagation can be estimated by applying a load. Three crack configurations were experimented on such that the results can be compared for various cases. The experimental process was design to follow the realistic loading conditions of an aircraft attachment lug closely. A tensile test was conducted on each crack configuration until it fails, giving the ultimate tensile strength of each configuration. After that, fatigue tests were conducted using specific percentages of the ultimate load, following a marker load history. This loading leaves striation marks on the fracture surface of the specimen as the crack propagates from the initial fabricated crack. These lines correspond to differing amplitudes of the periodic load sequence of the fatigue test. Pictures of the fracture surface were taken using a digital microscope camera, and its clarity enhanced using Photoshop. The lines were measured and analysed. The data obtain were processed through known equations and values to obtain the stress intensity factor of the various cracks.
URI: http://hdl.handle.net/10356/64931
Rights: Nanyang Technological University
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:MAE Student Reports (FYP/IA/PA/PI)

Files in This Item:
File Description SizeFormat 
Stress Intensity Factor of Cracks in Lugs.pdf
  Restricted Access
Main article4.85 MBAdobe PDFView/Open

Page view(s) 50

121
checked on Oct 21, 2020

Download(s) 50

14
checked on Oct 21, 2020

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.