Title: Synthesis and characterisation of manganese ferrite oxides for use in pseudocapacitive super capacitors as electrode materials
Authors: Quah, Ivan Tian Min
Keywords: DRNTU::Engineering
Issue Date: 2016
Abstract: Manganese Ferrite Oxides were synthesis in a bid to ascertain their specific capacitance for the use as supercapacitor electrodes. 5 samples of varying composition in the form of MnxFe3-xO4 were synthesised via chemical co-precipitation and post-annealing. Said 5 samples had x values of 0.5, 1, 1.5, 2 and 2.5 and were put under electrochemical and materials characterisation using techniques such as cyclic voltammetry, TEM and XRD. The cyclic voltammetry was conducted using a 3 electrode system with 1M of KOH as the electrolyte. The highest specific capacitance measured was from Mn1.5Fe1.5O4 of 114.35 F/g and an increasing trend was observed for the first 3 samples, namely Mn0.5Fe2.5O4, MnFe2O4 and Mn1.5Fe1.5O4. A decrease in Cs was subsequently observed for the next sample followed by an increase for the last sample. Said phenomena of decrease/increase could not be adequately explained however, to explain the phenomena; several reasons were put forward such as, insufficient amount of Mn3+ and Fe3+ ions and the presence of an unidentified phase.
URI: http://hdl.handle.net/10356/66347
Rights: Nanyang Technological University
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:MSE Student Reports (FYP/IA/PA/PI)

Files in This Item:
File Description SizeFormat 
FYP_REPORT_QUAH_TIAN_MIN_IVAN_U1221603F.pdf
  Restricted Access
FYP Report2 MBAdobe PDFView/Open

Page view(s)

164
Updated on Jun 24, 2021

Download(s)

11
Updated on Jun 24, 2021

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.