Title: Fabrication of transparent quantum dot fluorescence film
Authors: Zhou, Chengzhi
Keywords: DRNTU::Engineering::Materials
Issue Date: 2017
Abstract: A simple method of fabricating fluorescence quantum-dot-polypropylene (QD-PP) composite was demonstrated. The manufacturing process was as easy as direct coating of the porous polypropylene film with concentrated QD solution. The QD-PP films exhibited very bright fluorescence, high stability and flexibility. Annealing of the QD-PP films enabled the encapsulation of the QDs within the polymer structure and obtain highly transparent composite films. The relationship between annealing condition and the performance of the QD-PP film was determined by varying the annealing temperature from 110℃ to 140℃ and the annealing pressure from 0.2 T to 2.0 T. Various properties, including transparency, emission intensity and morphology information of the QD-PP film were characterized and studied. Generally speaking, the QD-PP films showed high transparency at high temperature. Whereas, transparency did not consistently increase with the increase of annealing pressure. While a maximum transparency was achieved, further increase of annealing pressure decreased the transparency. It was mainly due to the change of polymer structure and agglomeration of QDs. For all fabricated QD-PP films, a consistent emission peak was observed around 610 nm using a 450-nm activation light.
Rights: Nanyang Technological University
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:MSE Student Reports (FYP/IA/PA/PI)

Files in This Item:
File Description SizeFormat 
Final Year Project Report_Zhou Chengzhi1.pdf
  Restricted Access
3.56 MBAdobe PDFView/Open

Page view(s) 20

Updated on Nov 25, 2020

Download(s) 20

Updated on Nov 25, 2020

Google ScholarTM


Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.