Title: Fire resistance of engineered cementitious composite
Authors: Ng, Wee Feng
Keywords: DRNTU::Engineering::Civil engineering::Structures and design
Issue Date: 2017
Abstract: High strength engineered cementitious composite (HSECC) is a new material created through the combination of high strength concrete and normal engineered cementitious composite (NECC). The alteration has shown improvement to the properties of NECC. However, there is hardly any data on the behaviour of HSECC after exposure to elevated temperatures. Therefore, to examine the fire performance of HSECC, uniaxial compression test was conducted on HSECC and NECC after heating for comparison. The residual compressive properties of the heated specimens were examined in this study. Upon observation, it is gathered that HSECC is prone to shrinkage and surface cracking after exposure to temperature above 400°C. Furthermore, although HSECC specimen exhibited a higher compressive strength of 120 MPa at ambient temperature, it lacks the ability to retain its compressive strength and stiffness after heating as compared to NECC. Lastly, it is deduced that steel fibres are able to overcome abrupt failures of specimens after the melting of either PE or PVA fibres. Note that in the discussion of this study, NECC includes NECC-1 and NECC-2, and ECC includes both HSECC and NECC.
URI: http://hdl.handle.net/10356/71149
Rights: Nanyang Technological University
Fulltext Permission: restricted
Fulltext Availability: With Fulltext
Appears in Collections:CEE Student Reports (FYP/IA/PA/PI)

Files in This Item:
File Description SizeFormat 
st-31ab.pdf
  Restricted Access
2.68 MBAdobe PDFView/Open

Page view(s) 1

115
checked on Oct 24, 2020

Download(s) 1

23
checked on Oct 24, 2020

Google ScholarTM

Check

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.