dc.contributor.authorChua, Jinyu-
dc.description.abstractDissolving microneedles are considered as one of the most promising methods for transdermal drug delivery. However, the polymer and sugar materials used for fabrication generally have weaker mechanical properties as compared to insoluble metal or silicon. In other biomedical applications, nanoclay is incorporated into polymers to improve their mechanical properties. This has not yet been investigated in the field of dissolving microneedles. In this study, polymer-clay composite microneedles are fabricated by simple solvent casting from poly (lactic-co-glycolic acid) (PLGA) and bentonite, a non-toxic and biodegradable nanoclay. The effects of bentonite on the mechanical and in-vitro dissolution properties of the microneedles are investigated. PLGA microneedles were fabricated with 0, 5, 10 and 20wt.%-bentonite at molar concentration of 400mg/ml of organic solvent. With increasing bentonite amount used, fracture force significantly increased with bentonite incorporation. Fracture force of 5wt.% is 0.0189N per needle, 3 times larger than 0.0057N of 0wt.%. This reinforcement effect of bentonite suggests that sufficient dispersion of bentonite in PLGA was achieved, despite higher degree of clay aggregates observed. Dissolution rate decreases with increasing bentonite amount used. 5wt.% microneedle patches have a 50% slower dissolution rate as compared to 0wt.% microneedle patches. In conclusion, PLGA-bentonite composite dissolving microneedles were successfully fabricated via the method of solution blending and solvent casting at room temperature. In future studies, nanoclay can be used as a viable modifier to improve mechanically weaker polymers and control rapidly dissolving polymers used for microneedle fabrication.en_US
dc.format.extent43 p.en_US
dc.rightsNanyang Technological University-
dc.titleDissolving microneedles for transdermal drug deliveryen_US
dc.typeFinal Year Project (FYP)en_US
dc.contributor.supervisorChen Pengen_US
dc.contributor.schoolSchool of Chemical and Biomedical Engineeringen_US
dc.description.degreeBachelor of Engineering (Chemical and Biomolecular Engineering)en_US
item.fulltextWith Fulltext-
Appears in Collections:SCBE Student Reports (FYP/IA/PA/PI)
Files in This Item:
File Description SizeFormat 
AY17-18 FYP report - Chua Jinyu - U1421052A.pdf
  Restricted Access
2.03 MBAdobe PDFView/Open

Page view(s) 50

Updated on Jul 23, 2024

Download(s) 50

Updated on Jul 23, 2024

Google ScholarTM


Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.