|Title:||Microstructure and mechanical properties of Cu-containing amorphous carbon nanocomposite thin films by a hybrid deposition technique||Authors:||Luo, Jingying
|Keywords:||Filter Cathodic Vacuum Arc
|Issue Date:||2017||Source:||Luo, J., Sun, D., Zhang, S., Qian, H., & Huang, J. (2017). Microstructure and mechanical properties of Cu-containing amorphous carbon nanocomposite thin films by a hybrid deposition technique. Nanoscience and Nanotechnology Letters, 9(4), 438-445. doi:10.1166/nnl.2017.2349||Series/Report no.:||Nanoscience and Nanotechnology Letters||Abstract:||Cu-containing amorphous carbon (a-C:Cu) films were deposited on Si (100) substrate by a hybrid process where co-operating of a filter cathodic vacuum arc (FCVA) and a magnetron sputtering (MS). Cu content was tuned by changing the Cu MS power density from 0 to 4.93 W/cm2. The results show that metallic Cu exists in crystal with grain size 4–8 nm and there is no carbide formation. Incorporation Cu promotes graphitization of amorphous carbon matrix where C=C (sp 2) increases from 56% to 64%, whilst C–C (sp 3) decreases from 42% to 31%. Raman results show Id/Ig ratio increases from 0.71 to 1.45. Incorporation Cu from 0 to 16.86 at.% decreases hardness from 45.84 to 17.29 GPa. Toughness indicated by plasticity, with increase of Cu from 0 to 13.48 at.%, the plasticity increases from 21% to 43%, further increase Cu to 16.86 at.% results in a plasticity decrease to 33%. The coefficient of friction increases from 0.120 to 0.140 with increase of Cu content from 0 to 16.86 at.%. All the as-prepared films show a high H/E ratio of ≥0.1 and high elastic recovery ≥0.57.||URI:||https://hdl.handle.net/10356/84626
|ISSN:||1941-4900||DOI:||10.1166/nnl.2017.2349||Rights:||© 2017 American Scientific Publishers. All rights reserved.||Fulltext Permission:||none||Fulltext Availability:||No Fulltext|
|Appears in Collections:||MAE Journal Articles|
Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.