Please use this identifier to cite or link to this item:
Title: A micromechanism study of thermosonic gold wire bonding on aluminium pad
Authors: Xu, Hui
Liu, Changqing
Silberschmidt, Vadim V.
Pramana, S. S.
White, Timothy John
Chen, Z.
Sivakumar, M.
Acoff, V. L.
Keywords: DRNTU::Engineering::Materials
Issue Date: 2010
Source: Xu, H., Liu, C., Silberschmidt, V. V., Pramana, S. S., White, T. J., Chen, Z., et al. (2010). A micromechanism study of thermosonic gold wire bonding on aluminium pad. Journal of applied physics, 108(11).
Series/Report no.: Journal of applied physics
Abstract: A micromechanism of thermosonic gold wire bonding was elaborated by examining its interfacial characteristics as a result of the bonding process, including the fragmentation of the native aluminum oxide layer on Al pads, and formation of initial intermetallic compounds (IMCs). It is found that the existence of an approximately 5 nm thick native oxide layer on original Al pads has a significant effect on the bonding, and the nucleation of IMCs during the bonding process must overcome this relatively inert thin film. Bonding strength was fundamentally determined by the degree of fragmentation of the oxide films, through which the formation of IMCs can be initiated due to the direct contact of the metal surfaces to be bonded. The extent of fracture the oxide layer was strongly influenced by the level of ultrasonic power, as at its high level alumina fragmentation becomes pervasive resulting in contiguous alloy interfaces and robust bonds. The IMCs formed at the interfaces were identified as Al4Al and AuAl2 with a thickness of 150–300 nm. The formation mechanism of such IMCs was explained by the effective heat of formation theory.
DOI: 10.1063/1.3514005
Rights: © 2010 American Institute of Physics. This paper was published in Journal of Applied Physics and is made available as an electronic reprint (preprint) with permission of American Institute of Physics. The paper can be found at the following DOI: One print or electronic copy may be made for personal use only. Systematic or multiple reproduction, distribution to multiple locations via electronic or other means, duplication of any material in this paper for a fee or for commercial purposes, or modification of the content of the paper is prohibited and is subject to penalties under law.
Fulltext Permission: open
Fulltext Availability: With Fulltext
Appears in Collections:MSE Journal Articles

Files in This Item:
File Description SizeFormat 
18. A micromechanism study of thermosonic gold wire bonding.pdf1.6 MBAdobe PDFThumbnail

Citations 5

Updated on Mar 6, 2021

Citations 5

Updated on Mar 8, 2021

Page view(s) 5

Updated on May 16, 2021

Download(s) 5

Updated on May 16, 2021

Google ScholarTM




Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.