Title: Effect of electromigration on interfacial reactions between electroless Ni-P and Sn–3.5% Ag solder
Authors: Kumar, A.
Teo, P. S.
He, Min
Chen, Zhong
Keywords: DRNTU::Engineering::Materials
Issue Date: 2004
Source: Kumar, A., He, M., Chen, Z., & Teo, P. S. (2004). Effect of electromigration on interfacial reactions between electroless Ni-P and Sn–3.5% Ag solder. Thin Solid Films, 462-463, 413-418.
Series/Report no.: Thin solid films
Abstract: Effect of electromigration on interfacial reactions between electroless Ni–P (EL-Ni) and eutectic Sn–3.5% Ag solder has been investigated. Sandwich-type reaction couples, Cu/EL-Ni/Sn–3.5% Ag/EL-Ni/Cu, having two EL-Ni/Sn–3.5% Ag interfaces were prepared with the help of reflow process. During reflow, Ni3Sn4 intermetallic formed at the EL-Ni/Sn–3.5% Ag interfaces with a dark thin Ni3P layer underneath it. The reaction couples were annealed at 160 and 180 °C for various durations with and without the passage of DC current of 1×103 A/cm2 density. It was found that current does not affect the stoichiometry of the intermetallics formed at the EL-Ni/Sn–3.5% Ag interfaces. The same Ni3Sn4 intermetallic formed in the samples annealed at both the temperatures with and without current. Formation of Kirkendall voids in the Ni3P layer showed that Ni diffuses from EL-Ni through the grain boundaries of Ni3P to form Ni3Sn4. It was observed that current retards the Ni3Sn4 growth at both the anode and cathode side interfaces at 180 °C, while no significant retardation was observed at 160 °C. This effect of electromigration on the EL-Ni/Sn–3.5% Ag interfacial reactions was due to the presence of Ni3P layer in between EL-Ni and Ni3Sn4.
DOI: 10.1016/j.tsf.2004.05.042
Rights: © 2004 Elsevier. This is the author created version of a work that has been peer reviewed and accepted for publication by Thin Solid Films, Elsevier. It incorporates referee’s comments but changes resulting from the publishing process, such as copyediting, structural formatting, may not be reflected in this document. The published version is available at: [].
Fulltext Permission: open
Fulltext Availability: With Fulltext
Appears in Collections:MSE Journal Articles

Files in This Item:
File Description SizeFormat 
34. Effect of Electromigration on Interfacial Reactions between Electroless Ni-P.pdf373.88 kBAdobe PDFThumbnail


Updated on Jun 18, 2020


Updated on Mar 5, 2021

Page view(s) 10

Updated on Mar 5, 2021

Download(s) 10

Updated on Mar 5, 2021

Google ScholarTM




Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.