Title: H2 and CH4 oxidation on Gd0.2Ce0.8O1.9 infiltrated SrMoO3-yttria-stabilized zirconia anode for solid oxide fuel cells
Authors: Xiao, Peng
Ge, Xiaoming
Zhang, Lan
Lee, Jong-Min
Wang, Jing-Yuan
Wang, Xin
Issue Date: 2012
Source: Xiao, P., Ge, X., Zhang, L., Lee, J.-M., Wang, J.-Y., & Wang, X. (2012). H2 and CH4 oxidation on Gd0.2Ce0.8O1.9 infiltrated SrMoO3–yttria-stabilized zirconia anode for solid oxide fuel cells. International Journal of Hydrogen Energy, 37(23), 18349-18356.
Series/Report no.: International journal of hydrogen energy
Abstract: Strontium molybdate (SrMoO3) as an electronic conductor was incorporated with yttria-stabilized zirconia (YSZ) to form an anode scaffold for solid oxide fuel cells. Gd0.2Ce0.8O1.9 (GDC) nanoparticles were introduced by wet impregnation to complete the Ni-free GDC infiltrated SrMoO3–YSZ anode fabrication. The effects of SrMoO3 on the electrode conductivity and GDC infiltration on the catalytic activity were examined. A pronounced performance improvement was observed both on wet H2 and CH4 oxidation for the 56 wt.% GDC infiltrated SrMoO3–YSZ. In particular, the polarization resistance decreased from 8 Ω cm2 to 0.5 Ω cm2 under wet H2 (3% H2O) at 800 °C with the introduction of GDC. Under wet CH4 at 900 °C, a maximum power density of 160 mW cm−2 was obtained and no carbon deposition was observed on the anode. It was found that the addition of H2O in the anode caused an increase of electrode ohmic resistance and a decrease of open circuit voltage. Redox cycling stability was investigated and only a slight drop in cell performance was observed after 5 cycles. These results suggest that GDC infiltrated SrMoO3–YSZ is a promising anode material for solid oxide fuel cells.
URI: https://hdl.handle.net/10356/96894
http://hdl.handle.net/10220/11558
ISSN: 0360-3199
DOI: 10.1016/j.ijhydene.2012.08.131
Rights: © 2012 Hydrogen Energy Publications, LLC.
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:ERI@N Journal Articles
SCBE Journal Articles

Google ScholarTM

Check

Altmetric


Plumx

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.