Title: Elastic modulus, hardness and creep performance of SnBi alloys using nanoindentation
Authors: Shen, Lu
Septiwerdani, Pradita
Chen, Zhong
Keywords: DRNTU::Engineering::Materials
Issue Date: 2012
Series/Report no.: Materials science and engineering: A
Abstract: A series of SnBi alloys with Bi concentration ranging from 3% to 70% have been studied by nanoindentation technique at room temperature. Constant strain rate (CSR) method was used to evaluate the elastic modulus, hardness and the creep stress exponent of the alloys. SnBi solid solutions with Bi concentration up to 10 wt% show significantly higher modulus and hardness than pure Sn. Small amount of Bi precipitates inside Sn-rich phase effectively enhance the hardness and creep resistance of the alloy; while such distribution of Bi particles has no effect on the elastic response of the matrix. The strain rate–stress relationship of the SnBi alloys has been evaluated in the range from 90 to 450 MPa. Three stress regions dominated by different rate-controlling mechanisms exist for the SnBi alloys with Bi concentration greater than 10%. At the high stress region (>370 MPa), dislocation glide dominates the creep rate where the stress exponents are greater than 10. At the intermediate stress region (200–370 MPa), dislocation climb is the dominant creep mechanism with stress exponents around 5–8. When fine lamellar structure is the dominant constituent of the microstructure, phase boundary sliding is identified as the rate-controlling mechanism in the low stress region (<200 MPa).
URI: https://hdl.handle.net/10356/97815
http://hdl.handle.net/10220/11161
DOI: 10.1016/j.msea.2012.07.120
Rights: © 2012 Elsevier B.V.
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:MSE Journal Articles

SCOPUSTM   
Citations 50

82
Updated on Mar 6, 2021

PublonsTM
Citations 50

67
Updated on Mar 3, 2021

Page view(s) 50

555
Updated on Mar 8, 2021

Google ScholarTM

Check

Altmetric


Plumx

Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.