Title: Carbon nanowires fabrications via top down approach
Authors: Tan, Chong Wei
Tay, Beng Kang
Keywords: DRNTU::Engineering::Electrical and electronic engineering
Issue Date: 2012
Source: Tan, C. W., & Tay, B. K. (2012). Carbon nanowires fabrications via top down approach. Journal of nanoscience and nanotechnology, 12(1), 707-713.
Series/Report no.: Journal of nanoscience and nanotechnology
Abstract: Carbon nanowires are fabricated by the Langmuir Blodgett (LB) method via the top down approach on amorphous carbon. Thick a-C films (500 nm to 1 μm) have been successfully deposited after the treatment on silicon. The anisotropic etching of carbon using reactive ion etching (RIE) has been verified giving near vertical sidewalls. The LB method for depositing monolayer requires a hydrophilic surface. Plasma treatment is being performed on the silicon oxide hard mask to reduce the surface energy thereby making the surface from hydrophobic to hydrophilic. PS balls which are being deposited by LB method have one disadvantage which is the low adhesion of the PS ball to the silicon oxide surface. This adhesion is being improved by subjecting the PS ball to annealing which changes the shape and increase the contact area between the PS balls and the silicon oxide surface. As carbon and PS ball is vulnerable to oxygen plasma, a modified recipe of CF4:Ar was being used to etch the silicon oxide hard mask. There is almost little chemical reaction of the CF4 on carbon and PS ball. Carbon nanowires were successfully fabricated using polystyrene (PS) balls of diameter 450 nm. Through a series of steps, carbon nanowire of 500 nm in length and diameter approximately 250 nm can be produced.
DOI: 10.1166/jnn.2012.5399
Fulltext Permission: none
Fulltext Availability: No Fulltext
Appears in Collections:EEE Journal Articles

Citations 20

Updated on Mar 7, 2021

Citations 20

Updated on Mar 7, 2021

Page view(s) 20

Updated on Jul 26, 2021

Google ScholarTM




Items in DR-NTU are protected by copyright, with all rights reserved, unless otherwise indicated.